Journals →  Chernye Metally →  2020 →  #9 →  Back

Metal science and metallography
ArticleName Influence of chemical composition and cooling parameters on kinetics of austenite decomposition in high-carbon steels
ArticleAuthor E. V. Parusov, V. A. Lutsenko, I. N. Chuiko, O. V. Parusov
ArticleAuthorData

Institute of Ferrous Metallurgy named after Z. I. Nekrasov (Dnepr, Ukraine):

E. V. Parusov, Cand. Eng., Senior Researcher, Head of the Dept., e-mail: xxdneprxx@gmail.com
V. A. Lutsenko, Dr. Eng., Leading Researcher
I. N. Chuiko, Cand. Eng., Senior Researcher
O. V. Parusov, Cand. Eng., Senior Researcher

Abstract

The kinetics of supercooled austenite decomposition depends on numerous factors, the most important of which are the chemical composition of the steel and the temperature-rate conditions of cooling. When carrying out the main technological operations of heat treatment of steel, the austenite decomposition occurs in most cases with a constant decrease in temperature, therefore, studies of the features of the behavior of austenite during continuous cooling are of great practical importance. The kinetics of austenite decomposition during continuous cooling in high-carbon steels have been studied. The features of the structure formation during continuous cooling in C80D2 and C82D steels alloyed with carbide-forming elements are shown. When carrying out a comparative analysis, C86D carbon steel was used as the reference one. The heating temperature of the samples was (1010–1030) ± 10 °C, which is higher than the temperatures traditionally used in practice and is due to the need to increase the stability of austenite by increasing the average austenite grain size before the start of cooling. For the steels under study, structural diagrams were constructed and a comparative analysis of the features of the austenite decomposition kinetics in relation to the reference steel C86D was carried out. For steels alloyed with carbide-forming elements (C80D2V, C82DV, C82DCr, C82DCrV), a significant decrease in the lower critical cooling rate is characteristic, which, at high degrees of overcooling, can lead to the formation of structures formed by intermediate and shear mechanisms. For cooling rates lower than the lower critical one, the amount of pearlite is maximum, however, there are 6 point pearlite areas in the steel structure, which is an unacceptable indicator. Cooling of С80D2V, С82DV, С82DCr, С82DCrV and С86D steels is recommended to be carried out in the intercritical area with rates Vmin = (0.7÷0.8) · Vmax to the temperature interval of pearlite transformation (ti – 15÷20 °C) followed by quasi-isothermal holding and further cooling. The research results made it possible to improve the industrial cooling modes of coiled steel to achieve at least 90% pearlite with 1 point in the steel structure.

keywords Kinetics of austenite transformations, structure, rolled coil products, high-carbon steel, carbide-forming elements, cooling rate
References

1. Popova L. Е., Popov А. А. Diagrams of the austenite transformation in steels and beta solutions in titanium alloys: a handbook (3rd ed., revised and supplemented). Moscow: Metallurgiya, 1991. 503 p.
2. Atkins M. Atlas of continuous cooling transformation diagrams for engineering steels. Rotherhan (Yorkshire): BSC, 1977. 260 p.
3. Clas W. Austenite transformation kinetics of ferrous alloys. Greenwich: Climax Molybdenum Company, 1979. 83 p.
4. Wever T. I., Rose A. S., Peter W. et al. Atlas zur Wärmebehandlung der Stähle. Düsseldorf: Berichtigter Nachdruck, 1961. 257 p.
5. Korchunov A. G., Gun G. S., Shiryaev O. P. Pivovarova K. G. Study of structural transformation of hot-rolled carbon billets for highstrength ropes for responsible applications via the method of thermal analysis. CIS Iron and Steel Review. 2017. Vol. 13. pp. 38–40.
6. Metallurgy and heat treatment of steel: 2nd edition. Edited by М. L. Bernshtein, А. G. Rakhshtadt. Moscow: Metallurgizdat. Vol. 1, 1961; Vol. 2, 1962. 1656 p.
7. Romanov P. V., Radchenko V. P. Transformation of austenite at continuous cooling of steel. Atlas of thermochemical diagrams. Novosibirsk: Izdatelstvo Sibirskogo otdeleniya AN SSSR, 1960. 230 p.
8. Sadovskiy V. D. Transformations of supercooled austenite. Atlas of diagrams. Sverdlovsk: Metallurgizdat, 1947. 56 p.
9. Tsutsui K., Terasaki H., Maemura T. et al. Microstructural diagram for steel based on crystallography with machine learning. Computational Materials Science. 2019. Vol. 159. pp. 403–411.
10. Lopatin А. V., Prokhorov А. V. Isothermal and thermokinetic transformations of supercooled austenite. Stal. 1941. No. 11-12. pp. 48–49.
11. Sychkov А. B., Zhigarev М. А., Nesterenko А. М. et. al. High-carbon wire rod for the manufacture of high-strength reinforcing ropes. Bendery: Poligrafist, 2010. 280 p.
12. ISO 16120:2017. Non-alloy steel wire rod for conversion to wire. Published: 05.2017.
13. Klimenko А. P., Karnaukh А. I., Burya А. I. et. al. Differential thermal analysis and heat treatment technologies. Dnepropetrovsk: Porogi, 2008. 323 p.
14. Lutsenko V. А., Golubenko Т. N., Lutsenko О. V., Glazunova N. А. The grain size of austenite in chromium-molybdenum-bearing steels after austenitization at different temperatures. Chernye Metally. 2016. No. 12. pp. 17–20.
15. Kawulok P., Podolinský P., Kajzar P. et al. The influence of deformation and austenitization temperature on the kinetics of phase transformations during cooling of high-carbon steel. Archives of Metallurgy and Materials. 2018. Vol. 63, Iss. 4. pp. 1743–1748.
16. Parusov V. V., Sychkov А. B., Sagura L. V. et. al. Development of a twostage cooling mode for wire rod made of C80D2 steel microalloyed with boron and vanadium. Metallurgicheskaya i gornorudnaya promyshlennost. 2011. No. 3. pp. 53–56.
17. Parusov E. V., Gubenko S. I., Klimenko A. P., Chuiko I. N., Sagura L. V. Features of the austenite decomposition kinetics and regularities of the steel С82DCrV structure formation during continuous cooling. Vestnik Pridneprovskoy gosudarstvennoy akademii stroitelstva i arkhitektury. 2018. No. 1. pp. 42–51.
18. GOST 8233–56. Steel. Microstructure standards. Introduced: 01.07.1957.
19. Lutsenko V. А., Parusov E. V., Vorobey S. A., Golubenko Т. N. About prospects for production of coil rolled metal with small diameters in modern wire mills. Chernye Metally. 2019. No. 10. pp. 47–52.
20. Parusov E. V., Klimenko A. P., Lutsenko V. A. et al. The influence of the heating temperature on the kinetics of the austenite dissolution of high-carbon steel C82DV. Physical Metallurgy and Heat Treatment of Metals. 2018. № 1. pp. 34–42.
21. Houndremont E. Handbuch der Sonderstahlkunde: translation from Germany. Edited by Zaymovsky A. S., Bernshtein M. L., Meskina V. S. In 2 vol., 2nd edition. Moscow: Metallurgiya, 1966. 1274 p.
22. Hossain R., Pahlevani F., Sahajwalla V. Effect of small addition of Cr on stability of retained austenite in high carbon steel. Materials Characterization. 2017. Vol. 125. pp. 114–122.
23. Shuwei Cao. Production Practice of C82DA High Carbon Steel Wire Rod for Conversion to Wire. 3rd International Conference on Material, Mechanical and Manufacturing Engineering. Advances in Engineering Research. 2015. pp. 147–150.

Language of full-text russian