ArticleName Investigation of formation the Ti – Al intermetallic compounds on the surface of TiAl(γ) alloy
DOI 10.17580/tsm.2017.01.09
ArticleAuthor Skakov M. K., Sagdoldina Zh. B., Stepanova O. A., Rakhadilov B. K.
ArticleAuthorData

National Nuclear Center of Republic of Kazakhstan, Kurchatov, Kazakhstan:

M. K. Skakov, Head of Institute of Nuclear Energy
B. K. Rakhadilov, Senior Researcher of Institute of Nuclear Energy

 

Shakarim State University of Semey, Semey, Kazakhstan:

Zh. B. Sagdoldina, PhD, e-mail: sagdoldina@mail.ru

O. A. Stepanova, Head of a Chair of Engineering Physics and Thermal Energetics

Abstract

This article shows the results of studies of intermetallic compounds formation on the surface of TiAl (γ) alloy after Al coating and subsequent vacuum annealing at the temperatures of 600 and 700 оC for 2 hours. The diffusion surface enrichment of TiAl (γ) aluminum is used to improve the hightemperature oxidation resistance of the alloy. By magnetron sputtering, the surface of the alloy Ti – 42Al – 2.5Cr – 1Nb – 0.7Si – 0.5B (% (at.)) was coated with Al (500 nm thickness). Phase composition and surface morphology of the alloy were studied after vacuum annealing. Processes occurring in the vacuum annealing cause the changes in the coating morphology with formation of “bumps”, which can serve as the preferred centers of formation of new Ti – Al compounds. Based on the analysis of the impact of excess Al atoms per lattice TiAl (γ), it is shown that the diffusion process takes place without the formation of structural vacancies, and the dominant structural defects are antisite defects (Al → Ti). According to this mechanism, the displacement of the aluminum atoms in direction to the crystal surface is accompanied by relaxation of the elastic energy associated with the distortion of the crystal lattice, which results in a change in the surface morphology of the sample after vacuum annealing. There was conducted the X-ray phase analysis of the surface layers of samples in parallel X-ray beam geometry by a sliding irradiation of the surface samples of X-ray beam at a small angle of incidence. The results of phase analysis of the surface of a thin layer showed formation of new Al3Ti and Al2Ti intermetallic compounds after annealing at 600 оC. Increasing of vacuum annealing temperature to 700 оC does not change the phase composition of the surface layer. However intensity of diffraction reflections increased regarding Al3Ti, TiAl and Al2Ti reflexes. Thus, the application of thin coatings on Al alloy surface TiAl(γ) and vacuum annealing can modify the surface properties of the structural phase of the alloy to form the new Ti – Al intermetallic compounds.

keywords Intermetallic, coating, titanium aluminide, vacuum annealing, phase, morphology, antisite defect
References

1. Yamaguchi M., Inui H., Ito K. High-temperature structural intermetallics. Acta materiala. 2000. Vol. 48. pp. 307–322.
2. Stolo N. S., Liu C. T., Deevi S. C. Emerging applications of intermetallics. Intermetallics. 2000. Vol. 8. pp. 1313–1320.
3. Nuria Cinca, Carlos Roberto Camello Lima, Jose Maria Guilemanya. An overview of intermetallics research and application: Status of thermal spray coatings. Journal of Materials Research and Technology. 2013. Vol. 2 (1). pp. 75–86.
4. Ilin A. A., Kolachev B. A., Polkin I. S. Titanium alloys. Composition, structure, properties : reference book. Moscow, 2009. 520 p.
5. Demenok A. O., Ganeev A. A., Demenok O. B., Kulakov B. A. The Choice of Alloying Elements for Titanium Aluminide Base Alloys. Vestnik YuUrGU. Seriya “Metallurgiya”. 2013. Vol. 13, No. 1. pp. 95–102.
6. Masao Miyake, Seiya Tajikara, Tetsuji Hirato. Fabrication of TiAl3 coating on TiAl-based alloy by Al electrodeposition from dimethylsulfone bath and subsequent annealing. Surface & Coatings Technology. 2011. Vol. 205. pp. 5141–5146.
7. Goral M., Swadzba L., Moskal G., Jarczyk G., Aguilar J. Diffusion aluminide coatings for TiAl intermetallic turbine blades. Intermetallics. 2011. Vol. 19. pp. 744–747.
8. Haanappel V. A. C., Stroosnijder M. F. Ion implantation as research tool for improving oxidation behaviour TiAl based intermetallic alloys. Surface Engineering. 1999 Vol. 15 (2).
9. Zhenyu Liu, Guodong Wang. Improvement of oxidation resistance of γ-TiAl At 800 and 900 оC in air by TiAl2 coatings. Materials Science and Engineering A. 2005. Vol. 397, No 1/2. pp. 50–57.
10. Liu J., Dahmen M., Ventzke V., Kashaev N., Poprawe R. The effect of heat treatment on crack control and grain refinement in laser beam welded b-solidifying TiAl-based alloy. Intermetallics. 2013. Vol. 40. pp. 65–70.
11. Kolachev B. A., Elagin V. I., Livanov V. A. Metal science and thermal treatment of metals and alloys : tutorial for universities. Forth edition. Moscow : MISiS, 2005. 432 p.
12. Nakajima H., Sprengel W., Nonaka K. Diffusion in intermetallic compounds. Intermetallics. 1996. Vol. 4. pp. 17–28.
13. Sprengel W., Oikawa N., Nakajima H. Single-phase interdiffusion in TiAl. Intermetalics. 1996. Vol. 4. pp. 185–189.
14. Fu C. L., Yoo M. H. Bonding mechanisms and point defects in TiAI. Intermetallics. 1993. Vol. 1. pp. 59–63.
15. Mishin Y., Herzig Chr. Diffusion in the Ti – Al system. Acta Materialia. 2000. Vol. 48. pp. 589–623.
16. Lyakishev N. P. Condition diagrams of double metallic systems. Moscow : Mashinostroenie, 1996. 498 p.

17. Luo J. S., Li K., Li X. B., Shu Y. J., Tang Y. J. Phase evolution and alloying mechanism of titanium aluminide nanoparticles. Journal of Alloys and Compounds. 2014. Vol. 615. pp. 333–337.
18. Sagdoldina Zh. B., Mamaeva A. A. Phase transformations of Ti – Al system after ionic implantation and further thermal annealing. Tsvetnye metally. 2010. No. 4. pp. 82–84.
19. Chu M. S., Wu S. K. The improvement of high temperature oxidation of Ti – 50Al by sputtering Al film and subsequent interdiffusion treatment. Acta Materialia. 2003. Vol. 51. pp. 3109–3120.
20. Leyens C., van Liere J. W., Peters M., Kaysser W. A. Magnetron-sputtered Ti – Cr – Al coatings for oxidation protection of titanium alloy. Surface and Coatings Technology. 1998. Vol. 108/109, No. 1–3. pp. 30–35.

Language of full-text russian
Full content Buy
Back