ArticleName Influence of hot isostatic pressing on structure and mechanical properties of castings made of high-strength sparingly alloyed aluminium alloy ATs6N0.5Zh (АЦ6Н0,5Ж) with increased content of lead
DOI 10.17580/tsm.2016.09.13
ArticleAuthor Shurkin P. K., Akopyan T. K., Korotkova N. O.
ArticleAuthorData

National University of Science and Technology “MISiS”, Moscow, Russia:

P. K. Shurkin, Post-Graduate Student, e-mail: pa.shurkin@yandex.ru
N. O. Korotkova, Post-Graduate Student of a Chair of Foundry Technologies and Material Art

Baikov Institute of Metallurgy and Material Science, Russian Academy of Sciences, Moscow, Russia:

T. K. Akopyan, Researcher

Abstract

This paper describes the possibility of increasing the mechanical properties by hot isostatic pressing (HIP) operation of the castings made of high strength sparingly alloyed aluminum alloy (based on the Al – Zn – Mg – Cu – Ni – Fe system), which was produced using a low-grade zinc with high content of lead and iron impurities. We obtained the chill castings, which were subsequently subjected to hardening heat treatment (quenching followed by an artificial aging to the maximum strength). Part of the party of castings was preliminary subjected by the HIP treatment, and then also heat treated to the maximum strength. The microstructural studies using a scanning electron microscope shown that the structure of castings, which are not subjected to HIP, contains a large amount of fine lead inclusions. After barothermal treatment the microstructure takes the typical form for high strength nikalins with iron content, and lead inclusions are found significantly less. The density of castings after the HIP increases and becomes close to the theoretical value since the porosity is eliminated almost completely. According to the results of tensile test, the castings, which were not subjected to the HIP, are very brittle, and most of them are destroyed without elongation. The improvement of structure after the HIP provides the increase of properties. So the strength of castings increased by more than 60 MPa and the ductility increased 10 times more. It is also important to note the significant reduction of the mechanical properties values scatter. In particular, the scatter decreases more than two times for elongation and more than 90% for tensile strength. The fracture surface after the tensile test of the samples, which were subjected to the HIP treatment, contains numerous dimples and has a ductile character of fracture. In contrast, the fracture surface of the samples, which were not subjected to the HIP treatment, is characterized by an arrangement of the lead inclusions at the grain boundaries, which is the reason of the brittle intergranular fracture.
This paper was written within the Subsidiary Agreement No. 14.578.21.0039 (unique identifier of the project RFMEFI57814X0039; the Ministry of Education and Science of Russian Federation) within the realization of the Federal Target Program “Investigations and developments of the priority ways of development of scientific-technological complex of Russia for 2014–2020”.

keywords High-strength aluminium alloys, microstructure, castings, hot isostatic pressing (HIP), mechanical properties, nickalyns, lead impurity
References

1. Belov N. A. Fazovyy sostav promyshlennykh i perspektivnykh alyuminievykh splavov (Phase composition of industrial and prospective aluminium alloys). Moscow : MISiS, 2010. 511 p.
2. Belov N. A., Shcherbakov M. V., Belov V. D. O tekhnologichnosti vysoko prochnogo ekonomnolegirovannogo nikalina ATs6N0.5Zh pri lite, prokatke i svarke (About the workability of high-strength sparingly alloyed nickalyn ATs6N0.5Zh (ATs6N0,5Zh) during the casting, rolling and welding). Tsvetnye Metally = Non-ferrous metals. 2011. No. 12. pp. 94–98.
3. Akopyan T. K., Belov N. A., Kaybyshev R. O., Alabin A. N. Vliyanie zhidkostnogo goryachego izostaticheskogo pressovaniya na strukturu i svoystva novogo ekonomnolegirovannogo vysokoprochnogo liteynogo alyuminievogo splava ATs6N0.5Zh (Influence of liquid hot isostatic pressing on structure and properties of new lean alloyed high strength casting aluminum alloy Al6Zn0.5Ni (ATs6N0.5Zh) on the basis of Al – Zn – Mg – Ni – Fe system). Tsvetnye Metally = Non-ferrous metals. 2014. No. 11. pp. 104–109.
4. Akopyan T. K., Belov N. A. Approaches to the design of the new high-strength casting aluminum alloys of 7xxx series with high iron content. Non-ferrous Metals. 2016. No. 1. pp. 20–27. DOI: 10.17580/nfm.2016.01.04
5. GOST 4784–97. Alyuminiy i splavy alyuminievye deformiruemye Marki. (State Standard 4784–97. Aluminum and wrought aluminum alloys. Grades)
6. Kurdyumov A. V., Pikunov M. V. Proizvodstvo otlivok iz splavov tsvetnykh metallov : uchebnik dlya vuzov (Production of castings from non-ferrous metal alloys : tutorial for universities). Second edition, revised and enlarged. Moscow : MISiS, 1996. 504 p.
7. Vakhromov R. O., Tkachenko E. A., Antipov V. V. Zakonomernosti formirovaniya struktury i svoystv kovochnykh splavov sistemy Al – Zn – Mg – Cu s razlichnym soderzhaniem osnovnykh legiruyushchikh komponentov, mikrodobavok i primesey (Natural development of forming structure and properties of forgeable Al – Zn – Mg – Cu alloys having different content of main alloying elements, microadditives and impurities) Vestnik Samarskogo gosudarstvennogo aerokosmicheskogo universiteta = Samara State Aerospace University. 2012. No. 5 (36). pp. 215–222.
8. Stroganov G. B. Vysokoprochnye liteynye alyuminievye splavy (High-strength cast aluminium alloys). Moscow : Metallurgiya, 1985. 216 p.
9. Mondolfo L. F. Struktura i svoystva alyuminievykh splavov (Aluminium Alloys: Structure and Properties). Translated from English. Moscow : Metallurgiya, 1979. 640 p.
10. Belov A. F. Povyshenie kachestva i nadezhnosti fasonnykh otlivok putem vysokotemperaturnoy gazostaticheskoy obrabotki (Increasing of quality and reliability of mold castings by high-temperature gas-static treatment). Aviatsionnaya promyshlennost = Aviation Industry. 1986. No. 4. pp. 40–42.
11. Kopeliovich B. A. Issledovanie mekhanizma i kinetiki ustraneniya por v otlivkakh iz alyuminievykh splavov pri vysokotemperaturnoy gazostaticheskoy obrabotke (Investigation of mechanism and kinetics of hole removing in aluminium alloy castings with high-temperature gas-static treatment). Aviatsionnaya promyshlennost = Aviation Industry. 1988. No. 9. pp. 50–52.
12. Ceschini L., Morri A., Sambogna G. The effect of hot isostatic pressing on the fatigue behavior of sand-cast A356-T6 and A204-T6 aluminum alloys. Journal of materials processing technology. 2008. No. 204. pp. 231–238.
13. Staley J. T. Jr., Tiryakioglu M., Campbell John. The effect of hot isostatic pressing (HIP) on the fatigue life of A206-T71 aluminum castings. Materials Science and Engineering : A. 2007. No. 465. pp. 136–145.
14. Petrov P., Konstantinova S., Buchvarov G., Petrov I. Hot isostatic pressing treatment of AlSi7Mg aluminium alloy. Journal of Material Science and Technologies. 1994. No. 2. pp. 26–33.
15. Padalko A. G., Belov N. A., Veselov A. N., Talanova G. V. Termografiya fazovykh prevrashcheniy v doevtekticheskom silumine Al–7%Si–0,5%Mg pri vysokikh davleniyakh i temperature (Thermography of the phase transformations in a hypoeutectic Al–7% Si–0.5% Mg silumin at high pressures and temperatures). Metally = Russian metallurgy (Metally). 2009. No. 1. pp. 73–78.
16. Padalko A. G. Praktika goryachego izostaticheskogo pressovaniya neorganicheskikh materialov (Practice of hot isostatic pressing of inorganic materials). Moscow : Akademkniga, 2007. 267 p.
17. Kazuaki Mita, Takashi Ikeda, Masafumi Maeda. Phase diagram study of Fe – Zn intermetallics. Journal of Phase Equilibria. 2001. Vol. 22, No. 2. pp. 122–125.
18. GOST 1583–93. Splavy alyuminievye liteynye. Tekhnicheskie usloviya (State Standard 1583–93. Aluminium casting alloys. Specifications). Introduced: 1997–01–01. Moscow : Publishing House of Standards, 1993. (in Russian)

19. Belov N. A., Belov V. D., Alabin A. N., Zlobin G. S., Mishurov S. S. Vysokoprochnyy ekonomnolegirovannyy splav na osnove alyuminiya (High-strength sparingly alloyed alloy on the basis of aluminium). Patent RF, No. 2484168. Applied: 21.02.2012. Published: 10.06.2013. Bulletin No. 16.
20. GOST 1497–84. Metally. Metody ispytaniy na rastyazhenie (State Standard 1497–84. Metals. Methods of tension test). Introduced: 1986–01–01. (in Russian)
21. Yan Liu, Daming Jiang, Wenlong Xie, Jie Hu, Boran Ma. Solidification phases and their evolution during homogenization of a DC cast Al – 8.35Zn – 2.5Mg – 2.25Cu alloy. Materials Characterization. 2014. No. 93. pp. 173–183.
22. Yunjia Sh, Qinglin Pan, Mengjia Li, Xing Huang, Bo Li. Effect of Sc and Zr additions on corrosion behavior of Al – Zn – Mg – Cu alloys. Journal of Alloys and Compounds. 2014. No. 612. pp. 42–50.
23. Li Chun Mei, Chen Zhi Qian, Zeng Su Min, Cheng Nan Pu, Chen Tian Xiao. Intermetallic phase formation and evolution during homogenization and solution in Al – Zn – Mg – Cu alloys. Science China. 2014. No. 56. pp. 2827–2838.
24. Ibrahim Özbek. A study on the re-solution heat treatment of AA 2618 aluminum alloy. Materials Characterization. 2007. Vol. 58, No. 3. pp. 312–317.
25. F. Nový, M. Janecek, R. Král. Microstructure changes in a 2618 aluminium alloy during ageing and creep. Journal of Alloys and Compounds. 2009. Vol. 487, No. 1/2. pp. 146–151.
26. Pyu Kh. L. Mekhanicheskie svoystva materialov pod vysokim davleniem (Mechanical properties of materials under the high pressure). Volume 1. Under the editorship of E. G. Ponyatovskiy. Moscow : Mir, 1973. 296 p.
27. Mikhaylovskaya A. V., Kotov A. D., Pozdniakov A. V., Portnoy V. K. A highstrength aluminium-based alloy with advanced superplasticity. Journal of Alloys and Compounds. 2014. No. 599. P. 139–144.

Language of full-text russian
Full content Buy
Back