ArticleName Design of integrated diagram of aluminium alloys fatigue using acoustic emission method
DOI 10.17580/tsm.2016.04.10
ArticleAuthor Bashkov O. V., Bashkova T. I., Romashko R. V., Popkova A. A.
ArticleAuthorData

Komsomolsk-on-Amur State Technical University, Komsomolsk-on-Amur, Russia:

O. V. Bashkov, Assistant Professor, Head of a Chair of Materials Science and New Materials Technology, e-mail: bashkov_ov@mail.ru
T. I. Bashkova, Assistant Professor of a Chair of Materials Science and New Materials Technology
A. A. Popkova, Post-Graduate Student

 

Institute of Automation and Control Processes of Far Eastern Branch of Russian Academy of Sciences, Vladivostok, Russia:

R. V. Romashko, Leading Researcher

Abstract

This paper shows the investigation results of accumulation staging of damages and fatigue rupture of aluminium precipitation hardening alloy D16AT (Д16АТ) using acoustic emission method. The prime object of investigations was the development of the design method of integrated fatigue diagram, characterizing the stage accumulation of fatigue damages. There were carried out the investigations, aimed at the experimental check of the hypothesis about the staging of accumulation of damages, which may be set only according to the registered parameters of acoustic emission with separate analysis by the types of acoustic emission sources. In contrast to the research method, where the fractography analysis is carried out, application of acoustic emission method allows the significant reduction of the scope of testing. Identification of the sources of accumulation of damages (dislocations, micro- and marcocracks) was carried out by the results of earlier investigations of deformation staging in the conditions of static tension of various metals and alloys. The types of acoustic emission sources were considered on twoparameter distribution plane “acoustic emission signals energy — frequency parameter”. This paper shows the diagrams of separate accumulation of acoustic emission signals, obtained from various types of sources (dislocations, micro- and marcocracks). Fatigue accumulation stages were defined by the activity of various sources of acoustic emission signals. Integrated fatigue diagram of aluminium alloy D16AT was designed by the defined stages. The developed method considerably reduces the volume of the carried out fatigue tests and fractography investigations.
The investigation was carried out with the support of the grant of Russian scientific fund (project No. 14-12-01122) and the basic part of the state task (project No. 3817).

keywords Fatigue, stages, repeated stress, acoustic emission, source, dislocation, microcrack, macrocrack
References

1. Haigh B. P. Hysteresis in relation to cohesion and fatigue. Transactions of the Faraday Society. 1928. No. 24. pp. 125–137.
2. Ivanova V. S., Shanyavskiy A. A. Kolichestvennaya fraktografiya. Ustalostnoe razrushenie (Quantitative fractography. Fatigue rupture). Chelyabinsk : Metallurgiya, 1988. 400 p.
3. Kocanda S. Fatigue Failure of Metals (Fatigue and Fracture). Sijthoff and Noordhoff, 1978. 382 p.
4. Berkovits A., Fang D. Study of Fatigue Crack Characteristics by Acoustic Emission. Engineering Fracture Mechanics. 1995. Vol. 51 (3). pp. 401–416.
5. Harris D. O., Dunegan H. L. Continuous Monitoring of Fatigue Crack Growth by Acoustic Emission Techniques. Experimental Mechanics. 1974. Vol. 14, No. 2. pp. 71–91.
6. Shanyavskiy A., Banov M. Fatigue cracking and acoustic emission regularities in metals: crack origination and growth. Key Engineering Materials. 2014. Vol. 592/593. pp. 735–740.
7. Urbahs A., Shanyavskiy A., Banovs M., Carjova K. Evaluation of an acoustic emission criterion of under surface fatigue cracks development mechanism in metals. 16th International Conference Transport Means. October, 25–26, Kaunas, Lithuania, 2012. pp. 131–134.
8. Bashkov O. V., Panin S. V., Byakov A. V. Issledovanie vliyaniya tolshchiny azotirovannogo poverkhnostnogo sloya na stadiynost deformatsii i razrusheniya stali 12Kh18N10T metodom akusticheskoy emissii, korrelyatsii tsifrovykh izobrazheniy i analiza diagramm nagruzheniya (Investigation of the influence of nitrogenised surface layer thickness on the staging of deformation and rupture of steel 12Kh18N10T by acoustic emission method, correlation of digital images and analysis of loading diagrams). Fizicheskaya mezomekhanika = Physical mesomechanics. 2010. Vol. 13, No. 6. pp. 73–80.
9. Bashkov O. V., Bashkova T. I., Popkova A. A. The Use of Acoustic Emission for the Construction of a Generalized Fatigue Diagram of Metals and Alloys. Advances in Acoustic Emission Technology. Editors: G. Shen, Z. Wu, J. Zhang. 2015. Vol. 158. pp. 283–291. DOI: 10.1007/978-1-4939-1239-1_26
10. Bashkov O. V., Kim V. A., Evstigneev A. I., Popkova A. A., Bashkova T. I. Issledovanie kinetiki nakopleniya ustalostnykh povrezhdeniy v titanovom splave metodom akusticheskoy emissii (Investigation of the kinetics of fatigue ruptures accumulation in titanium alloy by acoustic emission method). Deformatsiya i razrushenie materialov = Deformation and fracture of materials. 2014. No. 4. pp. 41–47.
11. Krasilnikov V. A., Krylov V. V. Vvedenie v fizicheskuyu akustiku (Introduction in physical acoustics). Moscow : Nauka, 1984. 403 p.
12. Ivanova V. S., Terentev V. F. Priroda ustalosti metallov (Metal fatigue nature). Moscow : Metallurgiya, 1975. 456 p.
13. Terentev V. F. Ustalostnaya prochnost metallov i splavov (Fatigue strength of metals and alloys). Moscow : Intermet Engineering, 2002. 288 p.

Language of full-text russian
Full content Buy
Back