MATERIALS SCIENCE AND TECHNOLOGY. SEMICONDUCTORS
ArticleName Higher School of Economics The Influence of Illumination upon Electrophysical Parameters of CdTe Sample Contacts
ArticleAuthor A. G. Belov, V. A. Golubiatnikov, F. I. Grigor’ev, A. P. Lysenko, N. I. Strogankova, M. B. Shadov
ArticleAuthorData

Joint Stock Company «Giredmet»

A. G. Belov

M. B. Shadov

 

National Research University

V. A. Golubiatnikov

F. I. Grigor’ev
A. P. Lysenko

N. I. Strogankova

Abstract

Voltage−current characteristics (VIC′s) were investigated and electric resistivity and Hall coefficient measurements of high−ohmic cadmium telluride samples were made at room temperature. The samples were cut from ingots grown by traveling heater method and doped with chlorine (2 · 1017 cm−3 in load). Indium and gold were used as contact materials. Galvanomagnetic measurements were made at square−form samples using the Van der Pau method in magnetic fields B ≤ 1.5 Tl. The near−contact regions were illuminated by white light of variable intensity; the VIC′s were investigated also. In addition, the VIC′s were investigated when the sample was illuminated by monochromatic 480 nm light through gold−covered sides of the sample. The experiments showed that illumination of the near−contact region leads to a considerable decrease of sample resistance (by 2—3 orders of magnitude). The VIC′s had linear shapes and in most cases came through the origin of coordinates. With an increase in the light intensity the angle between the X−axis and the VIC straight line increased. Similar results were obtained when monochromatic light passed through gold−covered sides of the sample. We show that illumination of the near−contact region allows measuring the electrical resistivity and the Hall coefficient of the sample which is impossible without illumination.

keywords Cadmium telluride, near−contact region illumination, electrical resistivity, Hall coefficient, voltage−current characteristics
References

1. Jaeger, H. Transition resistances of ohmic contacts to p−type CdTe and their time−dependent variation / H. Jaeger, E. Seipp // J. Electron. Mater. − 1981. − V. 10, N 3. − P. 605—618.
2. Brinkman, A. W. Contacts to Cd/Zn/Te/Se compounds / A. W. Brinkman // Properties of Narrow Gap Cadmium−Based Compounds. − London (UK) : INSPEC, 1994. − P. 575—581.
3. Brun, D. Low resistance ohmic contact on n−CdTe / D. Brun, B. Daudin, E. Ligeon // Appl. Phys. Lett. − 1994. − V. 65, N 4. − P. 475—477.
4. Klevkov, Yu. V. Vliyanie passivacii poverhnosti p−CdTe v (NH4)2Sx na vol’t−ampernye harakteristiki kontaktov / Yu. V. Klevkov, S. A. Kolosov, A. F. Plotnikov // Fizika i tehnika poluprovodnikov. − 2006. − T. 40, N 9. − P. 1074—1078.
5. Klevkov, Yu. V. Elektrofizicheskie svoistva nelegirovannyh vysokoomnyh polikristallov n−CdTe / Yu. V. Klevkov, S. A. Kolosov, A. F. Plotnikov // Tam zhe. − 2007. − T. 41, N 6. − P. 670—673.
6. Kolosov, S. A. Izmenenie spektra elektronnyh sostoyanii v polikristallicheskom p−CdTe v rezul’tate otzhiga v Cd i estestvennogo stareniya / S. A. Kolosov, Yu. V. Klevkov, A. Yu. Klokov, V. S. Krivobok, A. I. Sharkov // Tam zhe. − 2009. − T. 43, N 11. − P. 1526—1532.
7. Kosyachenko, L. A. Osobennosti mehanizma elektroprovodnosti poluizoliruyushih monokristallov CdTe / L. A. Kosyachenko, O. L. Maslyanchuk, S. V. Mel’nichuk, V. M. Sklyarchuk, O. V. Sklyarchuk, T. Aoki // Tam zhe. − 2010. − T. 44, N 6. − P. 729—734.
8. Stafeev, V. I. Struktura i svoistva kontaktov CdxHg1−xTe−metall / V. I. Stafeev // Tam zhe. − 2009. − T. 43, N 5. − P. 636—639.
9. Blank, T. V. Mehanizmy protekaniya toka v omicheskih kontaktah metall−poluprovodnik / T. V. Blank, Yu. A. Gol’dberg // Tam zhe. − 2007. − T. 41, N 11. − P. 1281—1308.
10. Belyaev, A. P. Vliyanie metoda sinteza na svoistva plenok tellurida kadmiya, sintezirovannyh v rezko neravnovesnyh usloviyah / A. P. Belyaev, V. P. Rubec, V. V. Antipov, E. O. Eremina // Tam zhe. − 2010. − T. 44, N 7. − P. 978—980.
11. Meriuc, A. V. Osobennosti svetovoi vol’t−ampernoi harakteristiki dvustoronne chuvstvitel’nyh solnechnyh elementov na osnove tonkih bazovyh sloev CdTe / A. V. Meriuc, G. S. Hripunov, T. N. Shelest, N. V. Deineko // Tam zhe. − 2010. − T. 44, N 6. − P. 829—832.
12. Kolosov, S. A. Povedenie Bi v reshetke CdTe i effekt kompensacii v CdTe : Bi / S. A. Kolosov, V. S. Krivobok, Yu. V. Klevkov, A. F. Adiyatullin // Tam zhe. − 2013. − T. 47, N 4. − P. 538—545.
13. Kosyachenko, L. A. Self−compensation limited conductivity in semi−insulating indium−doped Cd0,9Zn0,1Te crystals / L. A. Kosyachenko, S. V. Melnychuk, O. L. Maslyanchuk, V. M. Sklyarchuk, O. F. Sklyarchuk, M. Fiederle, C. P. Lambropoulos // J. Appl. Phys. − 2012. − V. 112. − P. 013705.
14. Ruzin, A. Simulation of Schottky and ohmic contacts on CdTe/ A. Ruzin // Ibid. − 2011. − V. 109. − P. 014509.
15. Dubecky, F. Simulation of Schottky and ohmic contacts on CdTe / F. Dubecky, M. Dubecky // Ibid. − 2012. − V. 111. − P. 026102.

Language of full-text russian
Full content Buy
Back