ArticleName Technology of obtaining of solid alloys on the basis of titanium carbide by the saturation method, which excludes the volume shrinkage
ArticleAuthor Gurevich Yu. G.
ArticleAuthorData

Kurgan State University, Kurgan, Russia:

Yu. G. Gurevich, Professor of a Chair “Power Engineering and Technology of Metals”, e-mail: ygg@rambler.ru

Abstract

There is developed the technology of steel saturation of non-sintered carbide frames, which makes possible the complete maintenance of the sizes of component after the saturation. During the preliminary sintering of carbide frame and its following saturation by the alloyed steel, the volume shrinkage reaches 6–10%. As it was established by the preliminary experiments, during the saturation of rough (non-sintered) frame from the titanium carbide, the shrinkage volume decreased to its complete removal. However, the mechanical strength of carbide pressings during their traditional manufacturing is rather low, which complicates their transportation and organization of saturation. Various bindings were used for the purpose of increasing of strength of pressings from the titanium carbide. At the first stages of research, glycerin was chosen as the plasticizer and binding. There is substantiated, that the optimal content of glycerin is 9–13% (mas.). With such content of glycerin, pressings sustained the insignificant dynamic loadings and did not maintain their sizes. There is substantiated that the mixture of glycerin and petrolatum, which was applied as the binding of pressing of titanium carbide, provides its steel saturation. During the saturation of carbide frame with the temperature of 1465–1480 oC, the dissolution of titanium from carbide in steel is practically absent.

keywords Carbidosteel, glycerin, petrolatum, non-sintered frame, saturation, sizes maintenance, titanium carbide, pressing
References

1. Gurevich Yu. G., Antsiferov V. N., Savenykh L. M. et al. Iznosostoykie kompozitsionnye materialy (Wear-resistant composition materials). Yekaterinburg : Ural Branch of Russian Academy of Sciences, 2005. 216 p.
2. Narva V. C. The Influence of the Mechanical Activation of Powder Components. Proceedings of the 2nd International conference. Tallinn : Tallinn Technical University, 2000. pp. 157–158.
3. Gurevich Y., Rotermel P., Savinjih L. The new Wear Composition Carbide Pig Iron. Proceedings of the 2nd International conference. Tallinn : Tallinn Technical University, 2000. pp. 267–268.
4. Rotermel P., Savinjih L. The New resistant Composition Carbid Pig Iron. Proceedings of the 2nd International conference. Tallinn : Tallinn Technical University, 2000. p. 269.
5. Pavligo T. M., Plomodyalo L. G., Plomodyalo R. L., Svistun L. I. Milling of Carbide-Steel Powder Components and Their Mixtures in an Attrition Mill. Powder Metallurgy and Metal Ceramics. 2004. Vol. 43, No. 5/6. pp. 223–228.
6. Pavlygo T. M., Plomodyalo L. G., Plomodyalo R. L., Svistun L. I. Poroshkovaya metallurgiya — Powder Metallurgy and Metal Ceramics. 2004. No. 5/6. pp. 5–8.
7. Dudorova T. A., Rotermel P. V., Savinykh L. M. Iznosostoykost konstruktsionnykh detaley iz karbidostali (Wear-resistance of constructive compounds, made of carbidosteel). Progressivnye tekhnologii i sistemy mashinostroeniya. Mezhdunarodnyy sbornik nauchnykh trudov (Progressive technologies and systems of mechanical engineering. International collection of scientific proceedings). Donetsk : Donetsk State Technical University, 2000. Iss. 12. pp. 189–294.
8. Kulkov S. N., Gnyusov S. F. Karbidostali na osnove karbidov titana i volframa (Carbidosteels on the basis of carbides of titanium and tungsten). Tomsk : Publishing House of Scientific and Technical Literature, 2006. 240 p.
9. Gurevich Yu. G. Tekhnologiya Metallov — Technology of metals. 2007. No. 9. pp. 47–49.
10. Orlov V. N., Marfitsyn V. V., Gubanov I. F. Tekhnologiya mashinostroeniya — Mechanical engineering technology. 2004. No. 2. pp. 8.

Language of full-text russian
Full content Buy
Back